利用扫描电镜并结合元素能谱分析仪研究了热镀锌合金化超高强钢板在热冲压工况下镀层组织的演变过程,并对镀层粉化、剥落等损伤机理进行了讨论。结果表明:加热温度为600～680℃时,镀层的主要组织由δ1k相组成,温度升高至720℃后,δ1k相向Г相与液Zn转变,镀层中氧含量增加。当温度升高至810℃时,Г相与氧化物Zn O的含量达到顶峰,温度达到奥氏体温度870℃以上时, α-Fe (Zn)相成为主体,此时只有表面氧化物Zn O与少量的Г相存在。在成形前GA镀层内部存在预裂纹,由于液Zn的液态金属致脆导致裂纹的进一步扩展,随着淬火与成形的开展,在压应力的作用下使得镀层内部的裂纹沿横向扩展,造成了粉化以及剥落现象。
Abstract：The evolution process of the coating structure of hot-dip galvanized alloyed ultra-high strength steel plate under hot stamping conditions was studied using scanning electron microscopy(SEM) and energy disperse spectroscopy(EDS), and the damage mechanisms such as coating pulverization and peeling were discussed. The results indicate that when the heating temperature is 600-680 ℃, the main structure of the coating is composed of δ1k phases, when the temperature rises to 720 ℃, δ1kphases transform into Г Phase and liquid Zn, and the oxygen content in the coating increases. When the temperature rises to 810 ℃, the content of the Г phase and oxide Zn O reach the peak and when the temperature reaches above 870 ℃ for austenite, the α-Fe(Zn) phase becomes the main body, at this time only the surface oxide Zn O and a small amount of Г phases exist. Before forming, there are precracks inside the GA coating. Due to the embrittlement caused by the liquid metal of liquid Zn, the cracks further expand. As quenching and forming progress, under the action of compressive stress, the cracks inside the coating expand laterally, causing pulverization and peeling phenomena.
[1] LI J Q, TONG C P, ZHANG R, et al. A data-informed review of scientific and technological developments and future trends in hot stamping[J]. International Journal of Lightweight Materials and Manufacture, 2024, 7(2):327-343.
[2]王金凤,袁耀,李聪.激光拼焊异种超高强钢组织和力学性能[J].钢铁, 2022, 57(9):138-147.WANG Jinfeng, YUAN Yao, LI Cong, et al. Microstructures and mechanical properties of laser tailor-welded dissimilar super-high strength steel sheets[J]. Iron and Steel, 2022, 57(9):138-147.
[3]唐远寿,司宇,徐正萌,等.超高强度钢在汽车轻量化中的应用及研究进展[J].金属热处理, 2023, 48(10):247-254.TANG Yuanshou, SI Yu, XU Zhengmeng, et al. Application and research progress of ultra-high strength steel in automotive lightweight[J]. Heat Treatment of Metals, 2023, 48(10):247-254.
[4]李学涛,张杰,江社明,等.镀锌热冲压钢板成形过程中的裂纹产生及扩展[J].金属热处理, 2019, 44(3):202-206.LI Xuetao, ZHANG Jie, JIANG Sheming, et al. Research status on zinc-coated press-hardened steel[J]. Heat Treatment of Metals, 2019, 44(3):202-206.
[5]毕文珍,洪继要,王利.锌基镀层热冲压钢研究进展[J].宝钢技术, 2019,(6):38-44.BI Wenzhen, HONG Jiyao, WANG Li. Research status on zinccoated press-hardened steel[J]. Baosteel Technology, 2019,(6):38-44.
[6]黎敏,董妮妮,潘明,等.典型汽车用镀锌板耐腐蚀性能研究[J].表面技术, 2023, 52(4):295-303, 318.LI Min, DONG Nini, PAN Ming, et al. Corrosion Resistance of Typical Galvanized Plate for Automobile[J]. Surface Technology, 2023, 52(4):295-303, 318.
[7]吴琼兴.高润滑皮膜钢板的成形特性及在汽车覆盖件中的应用[J].锻压技术, 2017, 42(7):141-147.WU Qiongxing. Formability and application of lubricant treated steel sheets for automotive panels[J]. Forging&Stamping Technology, 2017, 42(7):141-147.
[8]刘丽艳,毕文珍,韦习成. Mn元素对热冲压钢镀锌层组织演变的影响[J].金属热处理, 2022, 47(4):93-99.LIU Liyan, BI Wenzhen, WEI Xicheng. Effect of Mn element on microstructure evolution of galvanized coating of hot stamping steel[J]. Heat Treatment of Metals, 2022, 47(4):93-99.
[9] OKAMOTO N L, MICHISHITA S, HASHIZUME Y, et al. Fracture toughness of the Fe-Zn intermetallic compounds measured by bend testing of chevron-notched single-crystal microbeams[J].ISIJ International, 2018, 58(9):1569-1577.
[10]刘诗文,孟宪陆,赵彦,等. Fe-Zn相图不同相区温度合金化锌镀层生长过程模拟[J].表面技术, 2023, 52(10):403-410, 429.LIU Shiwen, MENG Xianlu, ZHAO Yan, et al. Simulation of the growth process of galvannealed coatings at different zone temperature in Fe-Zn phase diagram[J]. Surface Technology, 2023, 52(10):403-410, 429.
[11] OKAMOTO L N, INOMOTO M, TAKEBAYASHI H, et al. Crystal structure refinement of theΓ-andΓ1-phase compounds in the Fe-Zn system and orientation relationships among α-Fe,ΓandΓ1phases in the coating layer of galvannealed steel[J]. Journal of Alloys and Compounds, 2018, 732:52-63.
[12]刘昕.热镀锌合金化钢板成形过程中镀层粉化机理研究[D].昆明:昆明理工大学, 2010.LIU Xin. The powdering mechanisem research of galvannealed steel sheet coating in forming[D] Kunming:Kunming University of Science and Technology, 2010.
[13]袁训华,陈本权,张启富,等.电解剥离过程中热镀锌合金化镀层的阳极溶解机制[J].材料热处理学报, 2015, 36(2):179-184.YUAN Xunhua, CHEN Benquan, ZHANG Qifu, et al. Mechanism of anodic dissolution of galvannealed coating during coulometric stripping[J]. Transactions of Materials and Heat Treatment,2015, 36(2):179-184.
[14]赵川翔,吴科,谢福永,等. 590MPa级合金化热镀锌双相钢剪边断面色差分析及改善[J].塑性工程学报, 2023, 30(8):235-241.ZHAO Chuanxiang, WU Ke, XIE Fuyong, et al. Analysis and improvement of color difference on trimming surface of 590 MPa galvannealed dual phase steel[J]. Journal of Plasticity Engineering,2023, 30(8):235-241.
[15]邓永刚,邸洪双,胡美源,等.基于三点弯曲试验研究合金化镀层剥落机制[J].东北大学学报(自然科学版), 2016, 37(1):49-53.DENG Yonggang, DI Hongshuang, HU Meiyuan, et al. Exfoliation mechanism of galvannealed coating by three point bend test[J]. Journal of Northeastern University(Natural Science),2016, 37(1):49-53.
[16] WANG K, ZHU B, WANG Z, et al. Successive phase and morphology evolution of galvannealed coating in hot stamping and diffusion modeling of alpha-Fe(Zn)/steel system considering the effect of Zn concentration[J]. Surface&Coatings Technology, 2019,380:125036.
基本信息:
中图分类号:TG174.4;TG306
引用信息:
[1]陈炜,黎小洲,曹一枢,等.热冲压工况下GA镀层组织演变及粉化现象[J].塑性工程学报,2025(03):46-52.
基金信息:
国家自然科学基金资助项目(51875263); 无锡市“太湖之光”科技攻关(产业化关键技术攻关)项目(WX0304B010301220019PD)
2025-04-07
2025-04-07
2025-04-07